JIS-SCMnM3B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.3-0.4 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 1.0-1.6 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Cr(%)(%) ≦0.2 | Mo(%)(%) 0.15-0.35 | Tegangan Hasil (Mpa)(%) ≧490 | Tegangan Tarik (Mpa)(%) ≧740 | Pemanjangan (%)(%) ≧13 |
Aplikasi
- Pengecoran Keluli Karbon Kekuatan Tegangan Tinggi dan Pengecoran Keluli Aloi Rendah untuk Struktur