JIS-SCPH32
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | W(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.2 | Si(%)(%) ≦0.6 | Mn(%)(%) 0.5-0.8 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.5 | Cr(%)(%) 2.00-2.75 | Mo(%)(%) 0.9-1.2 | W(%)(%) ≦0.1 | Cu(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) ≧480 | Pemanjangan (%)(%) ≧17 |
Aplikasi
- Tuangan Keluli untuk Perkhidmatan Suhu Tinggi dan Tekanan Tinggi
Kod Negara
- JIS
Standard
- G5151
Jenis Baja
- SCPH32
Jenis Baja yang Berkaitan