JIS-SFVAF5B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦0.5 | Mn(%)(%) 0.3-0.6 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Cr(%)(%) 4.0-6.0 | Mo(%)(%) 0.45-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 480-660 | Pemanjangan (%)(%) ≧18 |
Aplikasi
- Paduan Keluli Forging untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi
Kod Negara
- JIS
Jenis Baja
- SFVAF5B
Jenis Baja yang Berkaitan
Jenis Baja | Kod Negara | More | SFVAF5B | CNS | More | SFVAF5B | JIS | More | F5 | ASTM | More | 12CrMo-19-5 | DIN | More | X12CrMo7 | DIN | More |
---|