JIS-SQV3A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.25 | Si(%)(%) 0.15-0.30 | Mn(%)(%) 1.15-1.50 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) 0.7-1.0 | Mo(%)(%) 0.45-0.60 | Tegangan Hasil (Mpa)(%) ≧345 | Tegangan Tarik (Mpa)(%) 550-690 | Pemanjangan (%)(%) ≧18 |
Aplikasi
- Plat Keluli Paduan Mn-Mo dan Mn-Mo-Ni yang Dikuaskan dan Ditemper untuk Tangki Tekanan
Kod Negara
- JIS
Standard
- G3120
Jenis Baja
- SQV3A
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | SQV3A | 8973 | CNS | More | SQV3A | G3120 | JIS | More | Type C Class 1 | A533 | ASTM | More |
---|