JIS-SUSF316
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 10.0-14.0 | Cr(%)(%) 16.0-18.0 | Mo(%)(%) 2.0-3.0 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧520 | Pemanjangan (%)(%) ≧43 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- JIS
Standard
- G3214
Jenis Baja
- SUSF316
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F316 | 8702 | CNS | More | SUSF316 | G3214 | JIS | More | F316 | A182 | ASTM | More | F316 | A336 | ASTM | More | X5CrNi-Mo17-12-2 | 17440 | DIN | More |
---|