JIS-SUSF410C
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.6 | Cr(%)(%) 11.5-13.5 | Tegangan Hasil (Mpa)(%) ≧585 | Tegangan Tarik (Mpa)(%) ≦760 | Pemanjangan (%)(%) ≧14 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- JIS
Standard
- G3214
Jenis Baja
- SUSF410C
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F6A | A182 | ASTM | More | F6 | A336 | ASTM | More | SUSF410 | G3214 | JIS | More | SUSF410B | G3214 | JIS | More | SUSF410C | G3214 | JIS | More | SUSF410D | G3214 | JIS | More |
---|