ASTM-F310
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 19.0-22.0 | Cr(%)(%) 24.0-26.0 | Tegangan Hasil (Mpa)(%) ≧207 | Tegangan Tarik (Mpa)(%) ≧515 | Elongasi (%)(%) ≧30 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A182
Jenis Baja
- F310
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F310 | 8702 | CNS | Lagi | SUSF310 | G3214 | JIS | Lagi | F310 | A182 | ASTM | Lagi |
---|