ASTM-F6B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.02 | S(%)(%) ≦0.02 | Ni(%)(%) 1.0-2.0 | Cr(%)(%) 11.5-13.5 | Mo(%)(%) 0.4-0.6 | Cu(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧620 | Tegangan Tarik (Mpa)(%) 760-930 | Elongasi (%)(%) ≧16 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A182
Jenis Baja
- F6B
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SUSF6B | G3214 | JIS | Lagi | F6B | A182 | ASTM | Lagi |
---|