ASTM-F6B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.15 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦1.0 | P(%)(%) ≦0.02 | S(%)(%) ≦0.02 | Ni(%)(%) 1.0-2.0 | Cr(%)(%) 11.5-13.5 | Mo(%)(%) 0.4-0.6 | Cu(%)(%) ≦0.5 | Tegangan Hasil (Mpa)(%) ≧620 | Tegangan Tarik (Mpa)(%) 760-930 | Pemanjangan (%)(%) ≧16 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A182
Jenis Baja
- F6B