ASTM-F6NM
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.06 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 0.5-1.0 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) 3.5-4.5 | Cr(%)(%) 11.5-13.0 | Mo(%)(%) 0.5-1.0 | Tegangan Hasil (Mpa)(%) ≧620 | Tegangan Tarik (Mpa)(%) ≧790 | Elongasi (%)(%) ≧15 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- ASTM
Standar
- A182
Jenis Baja
- F6NM
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | SUSF6NM | G3214 | JIS | Lagi | F6NM | A182 | ASTM | Lagi |
---|