ASTM-F6NM
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.06 | Si(%)(%) 0.3-0.6 | Mn(%)(%) 0.5-1.0 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) 3.5-4.5 | Cr(%)(%) 11.5-13.0 | Mo(%)(%) 0.5-1.0 | Tegangan Hasil (Mpa)(%) ≧620 | Tegangan Tarik (Mpa)(%) ≧790 | Pemanjangan (%)(%) ≧15 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A182
Jenis Baja
- F6NM
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | SUSF6NM | G3214 | JIS | More | F6NM | A182 | ASTM | More |
---|