CNS-F321H
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-13.0 | Cr(%)(%) ≧17.0 | Ti(%)(%) 4xC%-0.6 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧520 | Elongasi (%)(%) ≧43 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- CNS
Standar
- 8702
Jenis Baja
- F321H
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F321H | 8702 | CNS | Lagi | SUSF321H | G3214 | JIS | Lagi | F321H | A336 | ASTM | Lagi | X6CrNi-Til8-10 | 17440 | DIN | Lagi | F321H | A182 | ASTM | Lagi |
---|