DIN-X6CrNi-Til8-10
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Elongasi (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.08 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.015 | Ni(%)(%) 9.0-12.0 | Cr(%)(%) 17.0-19.0 | Ti(%)(%) 5xC%-0.7 | Tebal (mm)(%) ≦160 | Tegangan Hasil (Mpa)(%) ≧190 | Tegangan Tarik (Mpa)(%) 500-700 | Elongasi (%)(%) ≧40 |
Aplikasi
- Flens/Bahu/Katup Baja Tahan Karat yang Ditempa dan Bagian dari Wadah Tekanan untuk Tinggi
Kode Negara
- DIN
Standar
- 17440
Jenis Baja
- X6CrNi-Til8-10
Jenis Baja Terkait
Jenis Baja | Standar | Kode Negara | Lagi | F321H | 8702 | CNS | Lagi | SUSF321H | G3214 | JIS | Lagi | F321H | A336 | ASTM | Lagi | X6CrNi-Til8-10 | 17440 | DIN | Lagi | F321H | A182 | ASTM | Lagi |
---|