C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.27 | Si(%)(%) 0.15-0.35 | Mn(%)(%) 0.5-1.0 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) 0.5-1.0 | Cr(%)(%) 0.25-0.45 | Mo(%)(%) 0.55-0.70 | V(%)(%) ≦0.05 | Tegangan Hasil (Mpa)(%) ≧450 | Tegangan Tarik (Mpa)(%) 620-790 | Pemanjangan (%)(%) ≧16 |
Aplikasi
- Paduan Keluli yang Didinginkan dan Ditemper untuk Bekas Tekanan
Kod Negara
- ASTM
Jenis Baja
- Class 2A