JIS-SFVQ2B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.27 | Si(%)(%) ≦0.4 | Mn(%)(%) 0.5-1.0 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Ni(%)(%) 0.5-1.0 | Cr(%)(%) 0.25-0.45 | Mo(%)(%) 0.55-0.70 | V(%)(%) ≦0.05 | Tegangan Hasil (Mpa)(%) ≧450 | Tegangan Tarik (Mpa)(%) 620-790 | Pemanjangan (%)(%) ≧14 |
Aplikasi
- Paduan Keluli yang Didinginkan dan Ditemper untuk Bekas Tekanan
Kod Negara
- JIS
Jenis Baja
- SFVQ2B
Jenis Baja yang Berkaitan
Jenis Baja | Kod Negara | More | SFVQ2B | CNS | More | SFVQ2B | JIS | More | Class 2A | ASTM | More |
---|