ASTM-F304L
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.035 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 8.0-13.0 | Cr(%)(%) 18.0-20.0 | Tegangan Hasil (Mpa)(%) ≧170 | Tegangan Tarik (Mpa)(%) ≦450 | Pemanjangan (%)(%) ≧30 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A336
Jenis Baja
- F304L
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F304L | 8702 | CNS | More | SUS304L | G3214 | JIS | More | F304L | A182 | ASTM | More | F304L | A336 | ASTM | More |
---|