JIS-SUS304L
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.03 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-13.0 | Cr(%)(%) 18.0-20.0 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧175 | Tegangan Tarik (Mpa)(%) ≧480 | Pemanjangan (%)(%) ≧29 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- JIS
Standard
- G3214
Jenis Baja
- SUS304L
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F304L | 8702 | CNS | More | SUS304L | G3214 | JIS | More | F304L | A182 | ASTM | More | F304L | A336 | ASTM | More |
---|