ASTM-F316L
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.035 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 10.0-15.0 | Cr(%)(%) 16.0-18.0 | Mo(%)(%) 2.0-3.0 | Tegangan Hasil (Mpa)(%) ≧170 | Tegangan Tarik (Mpa)(%) ≧185 | Pemanjangan (%)(%) ≧30 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A182
Jenis Baja
- F316L
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F316L | 8702 | CNS | More | SUS316L | G3214 | JIS | More | F316L | A182 | ASTM | More | F316L | A336 | ASTM | More | X2CrNi-Mo17-13-2 | 17440 | DIN | More |
---|