DIN-X2CrNi-Mo17-13-2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.03 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.045 | S(%)(%) ≦0.015 | Ni(%)(%) 11.0-13.0 | Cr(%)(%) 16.5-18.5 | Mo(%)(%) 2.0-2.5 | Tegangan Hasil (Mpa)(%) ≧235 | Tegangan Tarik (Mpa)(%) 450-700 | Pemanjangan (%)(%) ≧45 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- DIN
Standard
- 17440
Jenis Baja
- X2CrNi-Mo17-13-2
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F316L | 8702 | CNS | More | SUS316L | G3214 | JIS | More | F316L | A182 | ASTM | More | F316L | A336 | ASTM | More | X2CrNi-Mo17-13-2 | 17440 | DIN | More |
---|