ASTM-F321H
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦0.85 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-12.0 | Cr(%)(%) ≧17.0 | Ti(%)(%) 4xC%-0.6 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧485 | Pemanjangan (%)(%) ≧30 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- ASTM
Standard
- A336
Jenis Baja
- F321H
Jenis Baja yang Berkaitan