JIS-SUSF321H
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Ti(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.04-0.10 | Si(%)(%) ≦1.0 | Mn(%)(%) ≦2.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.03 | Ni(%)(%) 9.0-13.0 | Cr(%)(%) ≧17.0 | Ti(%)(%) 4xC%-0.6 | Tebal (mm)(%) ≦130 | Tegangan Hasil (Mpa)(%) ≧205 | Tegangan Tarik (Mpa)(%) ≧520 | Pemanjangan (%)(%) ≧43 |
Aplikasi
- Flange/Fitting/Valve Keluli Tahan Karat yang Ditempa dan Bahagian Bekas Tekanan untuk Tinggi
Kod Negara
- JIS
Standard
- G3214
Jenis Baja
- SUSF321H
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | F321H | 8702 | CNS | More | SUSF321H | G3214 | JIS | More | F321H | A336 | ASTM | More | X6CrNi-Til8-10 | 17440 | DIN | More | F321H | A182 | ASTM | More |
---|