ASTM-LF2
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | V(%) | Cu(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.3 | Si(%)(%) 0.15-0.30 | Mn(%)(%) 0.60-1.35 | P(%)(%) ≦0.035 | S(%)(%) ≦0.04 | Ni(%)(%) ≦0.4 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.12 | V(%)(%) ≦0.03 | Cu(%)(%) ≦0.4 | Tegangan Hasil (Mpa)(%) ≧250 | Tegangan Tarik (Mpa)(%) 485-655 | Pemanjangan (%)(%) ≧22 |
Aplikasi
- Paduan Karbon dan Keluli untuk Forging bagi Bekas Tekanan untuk Perkhidmatan Suhu Rendah
Lain-lain
- Nb : ≦0.02
Kod Negara
- ASTM
Standard
- A350
Jenis Baja
- LF2
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More | TStE 315 | DIN | More | SFL2 | 11067 | CNS | More | SFL2 | G3205 | JIS | More | LF2 | A350 | ASTM | More |
---|