DIN-TStE 315
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Ni(%) | Cr(%) | Mo(%) | Cu(%) | Al(%) | N(%) | Tebal (mm) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.16 | Si(%)(%) ≦0.45 | Mn(%)(%) 0.7-1.5 | P(%)(%) ≦0.03 | S(%)(%) ≦0.025 | Ni(%)(%) ≦0.3 | Cr(%)(%) ≦0.3 | Mo(%)(%) ≦0.08 | Cu(%)(%) ≦0.3 | Al(%)(%) ≧0.02 | N(%)(%) ≦0.02 | Tebal (mm)(%) 60≦t≦70 | Tegangan Hasil (Mpa)(%) ≧295 | Tegangan Tarik (Mpa)(%) 440-560 | Pemanjangan (%)(%) ≧23 |
Aplikasi
- Paduan Karbon dan Keluli untuk Forging bagi Bekas Tekanan untuk Perkhidmatan Suhu Rendah
Lain-lain
- Nb : ≦0.03
Kod Negara
- DIN
Jenis Baja
- TStE 315
Jenis Baja yang Berkaitan
Jenis Baja | Standard | Kod Negara | More |
TStE 315 |
DIN | More |
SFL2 |
11067 | CNS | More |
SFL2 |
G3205 | JIS | More |
LF2 |
A350 | ASTM | More |
---|