CNS-SFVA-F11A
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) ≦0.2 | Si(%)(%) 0.5-1.0 | Mn(%)(%) 0.3-0.8 | P(%)(%) ≦0.03 | S(%)(%) ≦0.03 | Cr(%)(%) 1.0-1.5 | Mo(%)(%) 0.45-0.65 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 480-660 | Pemanjangan (%)(%) ≧18 |
Aplikasi
- Paduan Keluli Forging untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi