DIN-13CrMo-4-4
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Tegangan Hasil (Mpa) | Tegangan Tarik (Mpa) | Pemanjangan (%) |
---|---|---|---|---|---|---|---|---|---|
C(%)(%) 0.08-0.18 | Si(%)(%) ≦0.35 | Mn(%)(%) 0.4-1.0 | P(%)(%) ≦0.04 | S(%)(%) ≦0.025 | Cr(%)(%) 0.70-1.15 | Mo(%)(%) 0.4-0.6 | Tegangan Hasil (Mpa)(%) ≧275 | Tegangan Tarik (Mpa)(%) 440-590 | Pemanjangan (%)(%) ≧22 |
Aplikasi
- Paduan Keluli Forging untuk Bekas Tekanan untuk Perkhidmatan Suhu Tinggi
Kod Negara
- DIN
Jenis Baja
- 13CrMo-4-4
Jenis Baja yang Berkaitan